Poly(Ethylene Oxide)-block-Polysulfone-block-Poly(Ethylene Oxide) / Poly(etherblock-amide) Composite Membrane for Carbon Dioxide Separation

  • Adekunle Omoniyi

Student thesis: Master's Thesis


This research study describes the gas separation performance of different sets of Polyethyleneoxide-block-Polysulfone-block-Polyethyleneoxide/poly(ether-block-amide) (PEO-b-PSU-b-PEO/Pebax) composite membranes for CO2 separation from N2 and CH4. Gas permeation properties of the membranes prepared were studied at ambient temperature (21oC) and 8bar. The dependence of gas flux and selectivity on pressure was explored for different pressures from 2.5 bar up to 19 bar also at ambient temperature. Pebax/PAN composite membranes have a range of CO2 permeance of 4467±274 GPU, 365±64 GPU for CH4 and 152±17 GPU for N2 with CO2/N2 and CO2/CH4selectivities ranges of 30 and 13 respectively. Improved CO2/N2 and CO2/CH4 selectivities coupled with flux reduction were obtained from the introduction of PEO-b-PSU-b-PEO films on Pebax/PAN composite membranes. The gas flux reduced to about one-tenth of Pebax/PAN membrane’s while the selectivities obtained for all the PEO-b-PSU-b- PEO/Pebax/PAN membrane range from 33 to 60 for CO2/N2 and 17 to 33 for CO2/CH4 as the thickness of PEO-b-PSU-b-PEO top layer increases.
Date of AwardJul 2012
Original languageEnglish (US)
Awarding Institution
  • Physical Sciences and Engineering
SupervisorKlaus-Victor Peinemann (Supervisor)


  • Polysulfone
  • Composite
  • Polyethylene Oxide
  • Membrane

Cite this