Morphological implications of the interphase bridging crystalline and amorphous regions in semi-crystalline polymers

Sanjay Rastogi, Ann E. Terry

Research output: Contribution to journalArticlepeer-review

24 Scopus citations


In semi-crystalline polymers a range of morphologies can be obtained in which a chain may traverse the amorphous region between the crystals or fold back into the crystals leading to adjacent or nonadjacent reentry, depending on the molecular architecture and crystallization conditions. This causes topological variations on the crystal surface and the occurrence of an interphase between the crystalline and amorphous domains, thus affecting the mechanical properties. In this chapter, we will discuss how the morphology within the interphase plays a prominent role in drawability, lamellar thickening and melting of thus crystallized samples. Normally, for linear polymers it is anticipated that extended chain crystals are thermodynamically most favorable, and ultimately, taking the example of linear polyethylene, it has been shown that such chains would form extended chain crystals. However, this condition will not be realized in a range of polymers upon crystallization from the melt, such as those which do not show lamellar thickening or in branched polymers where the side branches cannot be incorporated within the crystal and hence fully extended chains are not possible. From a series of experiments, it is shown that with sufficient time and chain mobility, although extended chain crystals are not achievable, the chains still disentangle and a thermodynamically stable morphology is formed with a disentangled crystallizable interphase. © Springer-Verlag 2005.
Original languageEnglish (US)
Pages (from-to)161-194
Number of pages34
JournalAdvances in Polymer Science
StatePublished - Dec 1 2005

Bibliographical note

Generated from Scopus record by KAUST IRTS on 2021-02-16


Dive into the research topics of 'Morphological implications of the interphase bridging crystalline and amorphous regions in semi-crystalline polymers'. Together they form a unique fingerprint.

Cite this