Abstract
We report significantly enhanced propylene/propane (C 3H 6/C 3H 8) selectivity in mixed matrix membranes fabricated using 6FDA-DAM polyimide and a zeolitic imidazolate framework (ZIF-8). Equilibrium isotherms and sorption kinetics of C 3H 6 and C 3H 8 at 35°C were studied on a 200nm commercially available ZIF-8 sample produced by BASF. Mixed matrix dense films were formed with 6FDA-DAM and 200nm BASF ZIF-8 particles. SEM imaging showed generally good adhesion between the ZIF-8 and 6FDA-DAM without the need for surface-treating ZIF-8. Pure gas permeation showed significantly enhanced mixed matrix ZIF-8/6FDA-DAM membrane C 3H 6/C 3H 8 separation performance over the pure 6FDA-DAM membrane performance. A C 3H 6 permeability of 56.2Barrer and C 3H 6/C 3H 8 ideal selectivity of 31.0 was found in ZIF-8/6FDA-DAM mixed matrix membrane with 48.0wt% ZIF-8 loading, which are 258% and 150% higher than the pure 6FDA-DAM membrane, respectively for permeability and selectivity. Permeation properties of C 3H 6 and C 3H 8 in ZIF-8 were back-calculated by the Maxwell model for composite permeability using pure gas permeation data, leading to a C 3H 6 permeability of 277Barrer and C 3H 6/C 3H 8 selectivity of 122. Mixed gas permeation also verified that selectivity enhancements were achievable in mixed gas environment by ZIF-8. © 2011 Elsevier B.V.
| Original language | English (US) |
|---|---|
| Pages (from-to) | 34-42 |
| Number of pages | 9 |
| Journal | Journal of Membrane Science |
| Volume | 389 |
| DOIs | |
| State | Published - Feb 2012 |
| Externally published | Yes |
Bibliographical note
KAUST Repository Item: Exported on 2020-10-01Acknowledged KAUST grant number(s): KUS-I1-011-21
Acknowledgements: This publication is based on work supported by Award No. KUS-I1-011-21, made by King Abdullah University of Science and Technology (KAUST).
This publication acknowledges KAUST support, but has no KAUST affiliated authors.