Calcium-doped sodium strontium barium niobate (SBNN, (Sr 0.6Ba 0.4) 4-xCa xNa 2Nb 10O 30, 0 ≤ x ≤ 0.5) ceramics were prepared by a conventional solid-state reaction method. SBNN showed 'filled' tetragonal tungsten-bronze structure with fully occupied A-sites. The tetragonal structure, as revealed by X-ray diffraction (XRD) and Raman spectroscopy, was not affected by the Ca-dopant. Effects of Ca-doping concentration on the phase transitions as well as ferroelectric, piezoelectric and pyroelectric properties of the SBNN ceramics were investigated. From the dielectric studies, two anomalies were observed, namely, a sharp normal ferroelectric transition at 260 °C and a broad maximum at round -110 °C. The later was affected by the Ca-doping concentration and its origin was discussed. At x = 0.3, the sample exhibited the highest pyroelectric coefficient of 168 μC/m 2 K and the largest piezoelectric coefficient (d 33) of 63 pC/N at room temperature. On the basis of our results, the pyroelectric properties of the SBNN were improved by Ca-doping. © 2012 Elsevier B.V. All rights reserved.
Bibliographical noteKAUST Repository Item: Exported on 2020-10-01
Acknowledgements: This research was supported by a research grant from the Hong Kong Polytechnic University (Grant No. GYJ72).
ASJC Scopus subject areas
- Materials Chemistry
- Mechanics of Materials
- Metals and Alloys
- Mechanical Engineering