Physical characterization of as-deposited and 1000 °C annealed Ta xAl 1-xN thin films was performed using several characterization techniques. X-ray diffraction metrology shows that the crystallographic phase and crystallinity of TaN and AlN films vary with composition. The unannealed TaN film was cubic TaN, while the annealed TaN was mixed hexagonal Ta 2N and hexagonal TaN. Both AlN films were hexagonal, with the annealed film having a higher crystalline fraction. However, Ta xAl 1-xN films displayed a relatively small change in crystalline fraction and crystallography. Well behaved capacitors were fabricated, and a work function of ∼5.0 eV was obtained.