A phosphonated phenol-formaldehyde-based high-temperature proton exchange membrane with intrinsic protonic conductors and proton transport channels

Xiaofeng Hao, Zhen Li, Min Xiao, Dongmei Han, Sheng Huang, Guan Xi, Shuanjin Wang, Yuezhong Meng

Research output: Contribution to journalArticlepeer-review

31 Scopus citations

Abstract

A high-temperature proton exchange membrane is a key component of high-temperature proton exchange fuel cells. However, its development has been impeded by problems such as mechanical stability issues and free phosphoric acid leaching. Here, phosphonated phenol-formaldehyde is first introduced into polybenzimidazole as a high-temperature proton exchange membrane, which synchronously has sufficient intrinsic protonic conductors and long-range proton transport channels. We propose replacing free phosphoric acid with immobilized phosphoric acid based on phosphonated phenol-formaldehyde, thus balancing the relationship between electrochemical performance and mechanical stability in a phosphoric-acid-doped membrane. Phosphonated phenol-formaldehyde with immobilized phosphoric acid can not only achieve anhydrous proton conductivity at high temperatures, but it can also mitigate the adverse impact of phosphoric acid on the swelling of the membrane. A composite 50PPF/PBI membrane with a low acid uptake level reached a peak power density of 607 mW cm−2 at 160 °C under fully anhydrous conditions. A single cell based on 50PPF/PBI MEA has a low attenuation rate over a period of 50 hours due to the eminent PA retention properties of the membrane. This result indicates a pathway to using phosphonated polymers as immobilized phosphoric acids in the field of high-temperature proton exchange membranes.
Original languageEnglish (US)
Pages (from-to)1138-1187
Number of pages50
JournalJOURNAL OF MATERIALS CHEMISTRY A
DOIs
StatePublished - Jan 1 2022
Externally publishedYes

Bibliographical note

Generated from Scopus record by KAUST IRTS on 2023-09-20

Fingerprint

Dive into the research topics of 'A phosphonated phenol-formaldehyde-based high-temperature proton exchange membrane with intrinsic protonic conductors and proton transport channels'. Together they form a unique fingerprint.

Cite this