2D matrix engineering for homogeneous quantum dot coupling in photovoltaic solids

Jixian Xu, Oleksandr Voznyy, Mengxia Liu, Ahmad R. Kirmani, Grant Walters, Rahim Munir, Maged Abdelsamie, Andrew H. Proppe, Amrita Sarkar, F. Pelayo García de Arquer, Mingyang Wei, Bin Sun, Min Liu, Olivier Ouellette, Rafael Quintero-Bermudez, Jie Li, James Fan, Li Na Quan, Petar Todorovic, Hairen TanSjoerd Hoogland, Shana O. Kelley, Morgan Stefik, Aram Amassian, Edward H. Sargent

Research output: Contribution to journalArticlepeer-review

258 Scopus citations

Abstract

Colloidal quantum dots (CQDs) are promising photovoltaic (PV) materials because of their widely tunable absorption spectrum controlled by nanocrystal size1,2. Their bandgap tunability allows not only the optimization of single-junction cells, but also the fabrication of multijunction cells that complement perovskites and silicon 3 . Advances in surface passivation2,4-7, combined with advances in device structures 8 , have contributed to certified power conversion efficiencies (PCEs) that rose to 11% in 2016 9 . Further gains in performance are available if the thickness of the devices can be increased to maximize the light harvesting at a high fill factor (FF). However, at present the active layer thickness is limited to ~300 nm by the concomitant photocarrier diffusion length. To date, CQD devices thicker than this typically exhibit decreases in short-circuit current (JSC) and open-circuit voltage (VOC), as seen in previous reports3,9-11. Here, we report a matrix engineering strategy for CQD solids that significantly enhances the photocarrier diffusion length. We find that a hybrid inorganic-amine coordinating complex enables us to generate a high-quality two-dimensionally (2D) confined inorganic matrix that programmes internanoparticle spacing at the atomic scale. This strategy enables the reduction of structural and energetic disorder in the solid and concurrent improvements in the CQD packing density and uniformity. Consequently, planar devices with a nearly doubled active layer thicknesses (~600 nm) and record values of JSC (32 mA cm-2) are fabricated. The VOC improved as the current was increased. We demonstrate CQD solar cells with a certified record efficiency of 12%.
Original languageEnglish (US)
Pages (from-to)456-462
Number of pages7
JournalNature Nanotechnology
Volume13
Issue number6
DOIs
StatePublished - Apr 23 2018

Bibliographical note

KAUST Repository Item: Exported on 2020-10-01
Acknowledged KAUST grant number(s): OSR-2017-CPF-3321-03
Acknowledgements: This publication is based in part on work supported by the Natural Sciences and Engineering Research Council of Canada, by the Ontario Research Fund Research Excellence Program and by Award OSR-2017-CPF-3321-03 made by King Abdullah University of Science and Technology (KAUST). Some of the GIWAXS/GISAXS measurements were performed at the Cornell High Energy Synchrotron Source (CHESS), supported by the NSF Award DMR-1332208. This work also made use of the South Carolina SAXS Collaborative using a SAXSLab Ganesha for the GISAXS/GIWAXS measurements, supported by the NSF Major Research Instrumentation program (award no. DMR-1428620). We thank U. Jeng for the GIWAXS tested at the National Synchrotron Radiation Research Center, Taiwan, China. We thank L. Goncharova for assistance with RBS measurements. We thank D. Kopilovic, E. Palmiano, L. Levina and R. Wolowiec for the technical support.

Fingerprint

Dive into the research topics of '2D matrix engineering for homogeneous quantum dot coupling in photovoltaic solids'. Together they form a unique fingerprint.

Cite this